Etude par émission acoustique de la dynamique des dislocations pendant la déformation cyclique de polycristaux d'aluminium

(Reçu le 5 août 1991, révisé le 23 janvier 1991, accepté le 10 février 1992)

Abstract
The cyclic plasticity of 5N polycrystalline aluminium have been studied at room temperature by measuring the continuous acoustic emission (A.E.) due to dislocations movements in the metal. In this study, original data have been obtained in the understanding of continuous A.E. sources. In comparison with classical interpretation given in the literature, the fact that dislocations are arranged according to a dislocation cell structure from the first cycle has been included in the analysis of the results. From this, it has been shown that the amplitude of the A.E. signal is not directly connected with the plastic strain rate prescribed to the fatigue sample and that the probability density function of dislocation loops created during the cycling can be determined.

Résumé
La plasticité cyclique de l'AI 5N polycristallin a été étudiée à la température ambiante à partir de mesures d'émission acoustique continue (E.A.). L'application de la technique de l'E.A. nous a permis d'obtenir des données originales quant aux mécanismes sources d'E.A. Par rapport aux interprétations classiques de la littérature, nous avons fait intervenir le fait que, dès les premiers cycles, une structure cellulaire de dislocations est établie. Nous montrons que l'amplitude du signal d'E.A. n'est plus liée directement à la vitesse de déformation plastique macroscopique. A partir de cette donnée, l'analyse des résultats d'E.A. permet d'obtenir des informations sur la fonction distribution des boucles de dislocations créées au cours de la déformation cyclique.