Zn influence on the plasticity of Cdo _0.96Zn _0.04Te

(Received 9 February 1990, revised 6 June 1990 and 21 June 1991, accepted 10 July 1991)

Abstract
Compression tests were performed on CdTe and Cd _0.96Zn _0.04Te to elucidate the mechanism through which Zn inhibits dislocation formation and motion during CdTe crystal growth, thus leading to a decreasing of the dislocation density. Uniaxial deformation experiments performed with CdTe and CdZnTe at constant strain rate within a wide temperature range ( ), have revealed a strong hardening effect of Zn within the whole temperature range. They also showed in CdZnTe a Portevin Le Chatelier effect between 770 K and 920 K confirmed by static strain aging experiments. Critical resolved shear stress (C.R.S.S.) values at and static strain aging results with CdZnTe point to size effect as the dominant interaction between Zn and dislocations. Thermal activation parameters were estimated in both materials.

Résumé
La déformation plastique a été utilisée comme approche des mécanismes par lesquels le zinc entrave le mouvement des dislocations au cours du processus de croissance cristalline de CdTe massif, réduisant ainsi la densité de dislocations. Les expériences de compression uniaxiale à vitesse constante, réalisées dans CdTe et CdZnTe entre 0,14 et 0,87 ont montré que le zinc est responsable d'un fort durcissement sur tout le domaine de températures étudié. Les expériences de déformation dans CdZnTe ont mis en évidence un phénomène du type Portevin Le Chatelier entre 770 K et 920 K, confirmé par des expériences de vieillissement statique. Les valeurs de scission critique à 195 K et les résultats des expériences de vieillissement statique dans CdZnTe sont compatibles avec un effet de taille dominant pour les interactions Zndislocations. Les paramètres d'activation thermique ont été estimés dans les deux matériaux.