Apports de la simulation numérique pour I'identification du comportement rhéologique des alliages d'aluminium par essai de bipoinçonnement

(Reçu le 20 juillet 1993, révisé le 7 décembre 1993, accepté le 7 janvier 1994)

Abstract
The modelling of rheological behaviour of aluminium alloys for hot metal forming is based on experimental tests. The plane strain compression tests under various thermomechanical conditions (effective strain, effective strain rate, temperature, ...) are used for such a procedure. It is shown that numerical modelling combined with classical approaches can advantageously help in testing interpretation. It is shown, for instance, that the friction coefficient or the thermal exchanges between the specimen and the dies can be accurately fitted. Furthermore, a comparison between the numerical results and micrographical observations shows that it is possible to use numerical results with a good confidence.

Résumé
L'identification du comportement rhéologique des alliages d'aluminium en vue de leur mise en forme à chaud par laminage nécessite la réalisation d'essais expérimentaux. Les essais de bipoinçonnement entre poinçons parallélépipédiques, réalisés sous diverses conditions thermomécaniques (déformation effective, vitesse de déformation effective et température) ont été retenus pour une telle identification. On montre que la simulation numérique des essais permet de corriger de manière substantielle les méthodes d'identification classiques basées sur des approches rigides viscoplastiques. On montre par exemple que les simulations numériques permettent d'ajuster le coefficient de frottement ou les conditions d'échange thermiques. Enfin, une comparaison entre résultats numériques et analyses micrographiques montre que l'on peut utiliser les résultats des simulations en vue de la prévision des évolutions microstructurales des alliages considérés.