Spectres infrarouges de verres à haute temperature par inversion de l'émission thermique de couches anisothermes

(Reçu le 2 octobre 1993, révisé le 3 février 1994 accepté le 23 février 1994)

Abstract
The infrared absorption spectra of silicate glasses and boric anhydrid at high temperature are worked out by means of an inverse technique of optimization from the emission spectra. The sample's emission spectral intensities are measured by a Fourier Transform lnfra-Red spectrometer. Specimens are plane parallel slabs which are deposited on a crusible. Their lower face is in contact of the crusible and isothermal but the upper one exchanges heat with the atmosphere by natural convection. In such conditions the glass slabs are submitted to high thermal gradients and the optimization method used is a non-linear constainted iterative method. The resulting spectra are compared to absorption spectra obtained by transmission spectrometry.

Résumé
Les spectres d'absorption infrarouge de verres de silicate et d'anhydride borique portés à haute température sont obtenus par inversion des spectres d'émission au moyen d'une méthode d'optimisation. Les luminances spectrales émises par les échantillons sont mesurées à l'aide d'un spectromètre à transformée de Fourier. Les échantillons sont des lames planes parallèles déposées dans un creuset ; leur surface inférieure est maintenue vers 1 000 K, alors que leur surface supérieure échange sa chaleur à l'air libre par convection naturelle. Dans ces conditions les lames sont soumises à de forts gradients thermiques. En présence de ces gradients une méthode itérative d'optimisation non linéaire contrainte est mise en oeuvre. On compare les résultats obtenus aux spectres d'absorption mesurés directement par spectrométrie de transmission.