NMR Investigations into Polydimethylsiloxane Adsorption on Silica Aggregates

(Received 8 June 1995, revised 23 October 1995, accepted 8 November 1995)

Abstract
Adsorption properties of polydimethylsiloxane on the surface of silica aggregates are studied from chemical microanalysis combined with proton magnetic relaxation measurements and from swelling measurements performed on mixtures. It is shown that polymer molecules, observed right after the preparation of mixtures, are strongly adsorbed on about 1/4 of the silica surface, only; they form islets. It is also shown that the number of contact points of a chain with the surface is proportional to during the progressive saturation of the silica surface; N is the number of monometric units in one chain.

Résumé
Les propriétés d'adsorption du polydimethylsiloxane sur la surface d'agrégats de silice sont étudiées par microanalyse chimique, par des mesures de relaxation magnétique des protons liés aux chaînes et par des mesures de gonflement des mélanges polymères-particules, utilisant un bon solvant. On montre qu'immédiatement après la préparation des mélanges, les chaînes solidement adsorbées n'occupent, sous la forme d'ilôts, que le quart de la surface de silice. On montre aussi que, pendant la saturation progressive de la surface, qui dure environ 3 mois à 343 K, le nombre de points de contacts d'une chaîne avec la silice est proportionnel à  ; N étant le nombre de maillons dans la chaîne.