Dielectric Properties of Hydrothermal Nickel-Zinc Ferrites

(Received 29 January 1996, revised 1 April 1996, accepted 18 April 1996)

Abstract
NiZn ferrites were hydrothermally prepared and sintered at different experimental conditions, leading to materials of composition Ni _0.34Zn _0.60Fe _2.06O ₄. An investigation of the dielectric properties over a wide frequency range showed the semiconductor character of the ferrites and the presence of a masked relaxation, revealed after a mathematical treatment. The relaxation was modeled using a Cole-Cole model and the parameters correlated with the microstructural evolution of the ferrites during the sintering. The contributions of hopping electrons and space charges to the total conductivity have been discussed.

Résumé
La méthode hydrothermale a été utilisée pour préparer des poudres de NiZn. Ces matériaux ont été synthétisés sous différentes conditions expérimentales. Après frittage, la composition est Ni _0,34Zn _0,60Fe _2,06O ₄. L'investigation des propriétés diélectriques, sur une large intervalle de fréquence, a démontré le caractère semiconducteur des ferrites et l'existence d'une relaxation masquée, mise en évidence après un traitement mathématique. Cette relaxation a été traitée par un modèle de type Cole-Cole et les paramètres corrélés à l'évolution microstructurale des ferrites, pendant le processus de frittage. Les contributions à la conductivités complexe dues aux électrons ("hopping") et aux charges d'espace ont été discutées.