Propriétés diélectriques et piézoélectriques de céramiques de Pb(Mg _1/3Nb _2/3O ₃ - PbTiO ₃ dopées

V. Bornand¹, A. El Bouchikhi², P. Papet¹ and E. Philippot<sup>1

1</sup>  Laboratoire de Physicochimie des Matériaux Solides, URA D0407-CNRS, UM II Sciences et Techniques du Languedoc, Place Eugène Bataillon, CC 003, 34095 Montpellier Cedex 5, France
²  Laboratoire de l'état solide, Faculté des Sciences, Kénitra, Maroc

(Reçu le 19 juin, révisé le 21 septembre 1995, accepté le 5 octobre 1995)

Abstract
0.65 Pb(Mg _1/3Nb _2/3)O ₃ - 0.35 PbTiO ₃ ceramics doped with lanthanum, iron and manganese oxides were synthesized. Experimental results showed the dopants by creating some points defects in the network of PMN-PT act on the microstructural development of ceramics and as a result on to dielectric constant and losses values. Moreover when the Mn ⁺⁴ ion were used as a dopant in a B site of the network, dielectrics losses were notably decreased allowing some using of this material in the field of acoustic wave at reasonable power.

Résumé
Différentes céramiques de composition 0,65 Pb(Mg _1/3Nb _2/3)O ₃ - 0,35 PbTiO ₃ (PMN-PT) dopées avec des oxydes de lanthane, de fer et de manganèse ont été synthétisées sous forme de composés massifs. Il ressort de cette étude que les dopants, en introduisant des défauts ponctuels dans le réseau, agissent sur la microstructure des céramiques et conditionnent ainsi les valeurs de la constante diélectrique et des pertes. L'ion Manganèse Mn ⁴⁺ en substitution dans les sites B de la structure des PMN-PT (35 % PT) permet d'abaisser de manière importante les pertes diélectriques du matériau, ce qui pourrait permettre d'utiliser cette céramique pour des applications de moyenne puissance.