Caractérisation de céramiques massives d'YBa Cu O par mesures ultrasonores et détermination précise des paramètres cristallins

(Reçu le 7 novembre 1990, révisé et accepté le 31 octobre 1991)

Abstract
In order to assess the influence of different processing cycles on the electrical properties, complementary information on the oxygen content and the state of the microstructure is required. We discuss the use of high resolution X-ray diffraction measurement to estimate the oxygen content and ultrasonic measurements for assessing the presence of microcracks which occur during cooling from the sintering temperature. In addition ultrasonic measurements as a function of temperature can be used to obtain information concerning the phase transformation, sintering and the origin of microcracks. Samples which have been submitted to different processing conditions are compared.

Résumé
Une caractérisation microstructurale poussée s'est avérée nécessaire en vue d'une bonne compréhension de l'influence des différentes phases d'élaboration sur les propriétés finales de céramiques massives d'YBa ₂Cu ₃O . Des mesures ultrasonores à température ambiante ont permis d'évaluer la microfissuration se produisant lors du refroidissement. Par ailleurs, des mesures similaires en fonction de la température ont fourni des informations concernant la densification, les changements de phase et les mécanismes d'apparition des microfissures. Dans l'optique d'un contrôle systématique de la teneur en oxygène, nous avons développé une méthode d'analyse par diffraction des rayons-X à haute résolution. Ainsi, des échantillons d'YBa ₂Cu ₃O réalisés selon différents procédés d'élaboration ont pu être comparés.