Extensive characterization of anisotropic conductors in the Montgomery geometry

(Received 1 February 1993, revised 21 November 1993, accepted 3 January 1994)

Abstract
In very anisotropic materials the transport properties of a single crystal may be equivalent to those of a long thin bar. In this geometry we show that an extension of the Montgomery method [1] allows a detailed discussion of the experimental results. It is then possible to establish the correct value of the anisotropy of the resistivity tensor. The method is used to show that in La ₂CuO _4+0.018, the conductivity is activated in the Cu-O planes while it results from variable range hopping process perpendicular to the planes as previously established.

Résumé
Dans le cas de matériaux très anisotropes, les propriétés de transport d'un monocristal peuvent être équivalentes à celle d'une longue barre de section quasi carrée. Dans cette géométrie, nous avons analysé en détail les erreurs introduites par l'emploi de la technique de Montgomery [1]. Nous proposons une extension de cette méthode. Dans ces conditions, nous montrons qu'une analyse complète peut aisément permettre de choisir une géométrie de test conduisant à la détermination de l'anisotropie réelle du matériau et de sa variation thermique. La méthode est utilisée pour montrer que, dans le composé La ₂CuO _4+0.018, la conductivité est activée dans les plans Cu-O alors que, perpendiculairement aux plans, nous avons montré précédemment qu'elle résulte d'un processus de sauts.