Réseaux de vortex dans Bi ₂Sr ₂Ca ₁Cu ₂O _x

(Reçu le 3 février 1994, révisé le 16 mai 1994, accepté le 24 mai 1994)

Abstract
Results of the defect influence on the flux line lattice in Bi ₂Sr ₂Ca ₁Cu ₂O _x single crystals are presented. These crystals, non irradiated or irradiated at GANIL with heavy ions (Pb ⁵⁶⁺, 6 GeV) have been decorated with Ni particles in the superconducting state using the Bitter technique. The defects involved are columnar defects. Resulting decorated flux line patterns have been characterized using scanning electron microscopy and computer image analysis. Disorder of the decorated flux line networks has been found to be strongly dependent on the defect density, which results from the irradiation. In order to characterize this disorder, a method for determining elastic energy terms in the deformation of flux line patterns has been investigated. This method can be applied if Fourier transforms of the decorated flux line patterns exhibit distinct reflections.

Résumé
Nous présentons une étude sur l'influence des défauts vis-à-vis du piégeage des lignes de flux magnétique dans des monocristaux de Bi ₂Sr ₂Ca ₁Cu ₂O _x. Ces monocristaux, non irradiés ou irradiés sur l'accélérateur du GANIL avec des ions (Pb ⁵⁶⁺) d'énergie 6 GeV ont été décorés dans l'état supraconducteur selon la technique de Bitter. Les réseaux de lignes de flux magnétique ont eté caractérisés par microscopie électronique à balayage et avec un analyseur d'images. Les résultats montrent que les réseaux de lignes de flux magnétique sont fortement dépendant de la densité de défauts résultant de l'irradiation. Pour caractériser l'état de désordre, nous avons appliqué une méthode de calcul de termes d'énergie élastique des réseaux de lignes de flux magnétique. Cette méthode ne peut être appliquée que si la transformée de Fourier des réseaux de vortex présente des réflexions discrètes.