Relations de phases et cristallogenèse de phases de Chevrel séliniées
(TR = Terre rare) : premiers résultats sur monocristal
F. Maho1, F. Le Berre1, O. Penã1, R. Horyn1 and A. Wojakowski2
1 Chimie du Solide et Inorganique Moléculaire, URA CNRS 1495, Université de Rennes I, 35402 Rennes Cedex, France
2 Institute for Low Temperature and Structure Research, Polish Academy Sciences, Wroclaw, Pologne
(Reçu le 3 février 1994, révisé le 18 juillet 1994, accepté le 4 octobre 1994)
Abstract
An approach to grow single crystals of chosen RE-Mo-Se Chevrel phase materials from a liquid phase was done. To reduce the
effects of compositional shifts due to incongruent melting (at 1 650-1 750
C), off-stoichiometric selenium-rich compositions were used. Prior to this, a detailed study of phase relations at 1 200
C was done and extended to 1 700
C. First preliminary magnetic and superconducting measurements were done on crystals containing RE = Gd, Ho, Er and Yb.
Résumé
La cristallogenèse de phases de Chevrel séléniés à base de terres rares (TRMo
6Se
8) a été réalisée avec succès pour TR = Gd, Ho, Er et Yb. La technique consiste en la fusion (non congruente) des compositions
riches en terres rares et en sélénium, dans des nacelles hermétiques, à 1 650-1 750
C. Une étude des relations de phases à 1 200
C et son extension à 1 700
C ont dû être préalablement effectuées. Les mesures préliminaires de propriétés magnétiques et supraconductrices de ces cristaux
ont été effectuées.