High Speed Deformation of the Poly(Ethylene Terephthalate)

(Received 13 January 1995, revised 12 June 1995, accepted 25 September 1995)

Abstract
Mechanical behaviour of amorphous and semi-crystalline polyethylene terephthalate films is studied over five decades of strain rates, at temperatures below and above the glass transition. The data were obtained by combining measurements from conventional Instron machine with data from a high-speed tensile machine. The activation parameters are determined and compared with the activation process of the relaxation. Different modes of failure have been identified and the occurrence of an intermediate mode between ductile and brittle failure is shown. The brittle-ductile transition is estimated for each testing conditions and compared to the adiabatic-isothermal transition.

Résumé
Le comportement mécanique du Poly(éthylène téréphthalate) amorphe et semi-cristallin est étudié sur plus de cinq ordres de grandeurs de vitesse de déformation, de part et d'autre de la température de transition vitreuse. Les mesures expérimentales sont réalisées à l'aide d'une machine de traction Instron, pour les faibles vitesses de déformation, et d'une machine servo-hydraulique pour les grandes vitesses. Les paramètres d'activation sont déterminés et comparés à ceux de la relaxation secondaire basse température . Différents modes de rupture sont identifiés; entre une rupture typiquement ductile et une rupture fragile, un mode de rupture intermédiaire est mis en évidence. La transition ductile-fragile est estimée pour chaque condition d'essai, et comparée à la transition isotherme-adiabatique.