Glide Dislocations Dissociation in Inversion Domain Boundaries of Plastically Deformed Aluminium Nitride

(Received 16 February 1996, revised 9 May 1996, accepted 3 June 1996)

Abstract
A ten per cent plastic deformation of polycrystalline aluminium nitride, at a temperature ranging from 1500 to 1650  C creates a new kind of intragranular defect. Observed by transmission electron microscopy, the look like torsion subboundaries created by dislocations with Burgers vectors and so nodes are dissociated into Shockley partials. They are located in the basal plane. In fact, these defects appear only in the plane areas of grown-in defects, the inversion domain boundaries. The formation of these faulted networks is interpreted as being the ultimate stage of the interactions between inversion domain boundaries and glide dislocations.

Résumé
Une déformation plastique de 10 % de nitrure d'aluminium polycristallin, entre 1500 et 1650  C introduit un nouveau type de défauts intragranulaires. Au microscope électronique par transmission, ils apparaissent comme des sous-joints de torsion créés par des dislocations de vecteurs de Burgers dont les noeuds triples sont dissociés en partielles de Shockley ; ils sont situés dans le plan de base. En fait, ces défauts ne se produisent que sur les parties planes de défauts originels, les parois de domaines d'inversion. La formation de ces réseaux fautés est analysée comme l'ultime stade des interactions entre parois de domaines d'inversion et dislocations de glissement.